Elaboration of high aspect ratio monocrystalline silicon suspended nanobridges by low temperature alkaline treatment of dry etched trenches - Physico-chimie des Matériaux et des Electrolytes pour l'Energie Laboratoire - - EA 6299 Accéder directement au contenu
Article Dans Une Revue Journal of Vacuum Science & Technology A Année : 2012

Elaboration of high aspect ratio monocrystalline silicon suspended nanobridges by low temperature alkaline treatment of dry etched trenches

Résumé

This paper describes the elaboration of high aspect ratio (250), high linear density (500 cm 1) suspended silicon nanobridges into low concentrated alkaline solutions. Trenches were first etched into silicon using the deep reactive ion etching STiGer process. These structures were immersed into low concentrated potassium hydroxide (KOH) or tetramethylammonium hydroxide (TMAH) solutions. The behaviors of KOH and TMAH as silicon trenches etching agents (kinetic and quality of etching) were studied to optimize the silicon nanowires (SiNWs) formation and the elaboration of the suspended structures. The limits of the SiNWs thickness in these conditions were also discussed.
Fichier non déposé

Dates et versions

hal-00655000 , version 1 (24-12-2011)

Identifiants

Citer

Thomas Defforge, Gaël Gautier, Thomas Tillocher, Remi Dussart, François Tran-Van. Elaboration of high aspect ratio monocrystalline silicon suspended nanobridges by low temperature alkaline treatment of dry etched trenches. Journal of Vacuum Science & Technology A, 2012, 30 (1), pp.010601. ⟨10.1116/1.3665217⟩. ⟨hal-00655000⟩
121 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More