Electrical property modulation of Au/Ba0.6Sr0.4TiO3/La0.7Sr0.3MnO3 structure by continuous composition spread Mn doping

Résumé

Composition spread Mn-doped Ba 0.6 Sr 0.4 Ti 1-x Mn x O 3 (BSTMx, 0 ≤x ≤ 0.05) thin films were prepared on La 0.7 Sr 0.3 MnO 3 /SrTiO 3 (LSMO/STO) layer by combinatorial pulsed laser deposition. When x is less than 3.3%, the BSTMx films are single phase according to X-ray diffraction data, and the Au/BSTMx/LSMO structure presents asymmetric transport properties. The asymmetry of the transport property gets weak with increasing Mn doping concentration. The reverse-bias current density of the Au/BSTMx/LSMO structure remains at a low value of 10 − 7 A/cm 2 , and the forward-bias current density reduces rapidly with the ascending doping content (x ≤ 1.8%). Further increasing the Mn content, the differences between the positive and reverse current densities become smaller, and almost vanish when the Mn content is greater than 3.8%, indicating the disappearance of the asymmetry of the transport property. The effects of the LSMO electrode, Au/BSTMx Schottky junction, BSTMx thin film, and BSTMx/LSMO interface on the whole electrical transport properties are discussed by virtue of the experimental and fitted impedance spectrums. Our results are helpful for insight into the doping mechanisms in perovskite oxides.
Fichier principal
Vignette du fichier
Qiu_Electrical property modulation of AuBST_LSMO.pdf (635.36 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-03844504 , version 1 (08-11-2022)

Identifiants

Citer

Jie Qiu, Guozhen Liu, Jerome Wolfman, Jie Xing. Electrical property modulation of Au/Ba0.6Sr0.4TiO3/La0.7Sr0.3MnO3 structure by continuous composition spread Mn doping. Ceramics International, 2022, 48 (8), pp.11786 - 11792. ⟨10.1016/j.ceramint.2022.01.038⟩. ⟨hal-03844504⟩
102 Consultations
48 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More